CROWN RESTORATIONS WITH MULTILAYER ZIRCONIUM OXIDE LIKE

CEREC MTL® Zirconia

With flexural strength of +850MPa, CEREC MTL® Zirconia is the esthetic zirconia that delivers the strength you need for the difficult posterior cases while providing natural esthetics suitable as you move into the smile line.

Pre-Treatment of the Restoration:

  • Sandblast the restoration

Material’s Flexural Strength2:

  • +850MPa 

Select achievable retention for cement recommendation:


LAB CROWN RESTORATIONS WITH MULTILAYER ZIRCONIUM OXIDE LIKE

Cercon® ht ML and Cercon® xt ML

Cercon® ht ML is the high translucent, hybrid zirconia multilayer for the combination of high strength and natural esthetics. From a single crown to a 14-unit bridge. No nesting restrictions even for widespan bridges. Excellent color matching for all 16 VITA®¹ shades and BL2.

Cercon® xt ML is an extra translucent zirconia for monolithic restorations at the highest level. Especially in the anterior region for up to 3-unit bridges up to the 2nd premolar. Available in all 16 VITA®¹ shades and BL2.

Pre-Treatment of the Restoration:

  • Sandblast the restoration

Material’s Flexural Strength2:

  • Cercon® xt ML: approx 750 MPa 
  • Cercon® ht ML : 750 – 1200 MPa

Select achievable retention for cement recommendation:

CROWN RESTORATIONS WITH ZIRCONIUM OXIDE LIKE

CEREC® Zirconia+

CEREC® Zirconia+ mono is a pre-dyed high strength translucent zirconium dioxide which is available in 10 classic VITA shades and does not require any further shading with a liquid. The material is dry milled and then sintered. After the sintering process, CEREC® Zirconia+ reaches its final size. The enlarged milling ensures high precision and accuracy of fit of the final restoration.

Pre-Treatment of the Restoration:

  • Sandblast the restoration

Material’s Flexural Strength2:

  • +1000 MPa 

Select achievable retention for cement recommendation:



LAB CROWN RESTORATIONS WITH ZIRCONIUM OXIDE LIKE

Cercon® ht, Cercon® xt or Cercon® base

Cercon® ht with True Color Technology sets new standards for zirconia when it comes to reproducing the classic 16 VITA®¹ and bleach shades (BL and BL2). It provides the highest level of color accuracy.

Cercon® xt  demonstrates extra high translucency in all 16 VITA®¹ and bleach shades (white and BL2) with True Color Technology.

Cercon® base is particularly suitable for covering discolored dies or titanium abutments and is available in 3 shades (white, medium and colored). 

Pre-Treatment of the Restoration:

  • Sandblast the restoration

Material’s Flexural Strength2:

  • Cercon® ht: approx. 1200 MPa
  • Cercon® xt : approx. 750 MPa
  • Cercon® base: approx.1200 MPa

Select achievable retention for cement recommendation:

CROWN RESTORATIONS WITH GLASS CERAMIC LIKE

CEREC Tessera™ Blocks

CEREC Tessera™ - Advanced Lithium Disilicate CAD/CAM blocks provide outstanding esthetics for a truly tooth-like restoration for single-unit full contour crowns, inlays, onlays and veneers. Up to 32% higher biaxial strength for restoration longevity and fast processing time for greater patient satisfaction and a more profitable procedure.

Pre-Treatment of the Restoration:

  • Etch with hydrofluoric acid
  • Silanize with Calibra® Silane Coupling Agent

Material’s Flexural Strength3:

  • +700MPa 

Select achievable retention for cement recommendation:


CROWN RESTORATIONS WITH GLASS CERAMIC LIKE

Celtra® Duo Blocks

With crystallites four to eight times smaller than lithium disilicate blocks, Celtra® Duo (ZLS) possesses an ultra-fine microstructure that combines high flexural strength with a high glass content, resulting in an impressive strength and beauty profile. Celtra® Duo can be processed either by mill and fire or mill and polish.

Pre-Treatment of the Restoration:

  • Etch with hydrofluoric acid
  • Silanize with Calibra® Silane Coupling Agent

Material’s Flexural Strength3:

  • 560 MPa (mill and fire) or 413 MPa (mill and polish) 

Select achievable retention for cement recommendation:

  1. VITA® is a registered brand of VITA Zahnfabrik GmbH
  2. 3-point flexural strength
  3. Biaxial flexural strength